Refine
Year of publication
Document Type
- Article (reviewed) (26)
- Conference Proceeding (10)
- Article (unreviewed) (2)
- Part of a Book (1)
Conference Type
- Konferenzartikel (10)
Language
- English (39) (remove)
Is part of the Bibliography
- yes (39) (remove)
Keywords
- Plastizität (11)
- Ermüdung (7)
- Mikrostruktur (6)
- Materialermüdung (5)
- Stahl (5)
- Thermomechanik (4)
- Eisenguss (3)
- Finite-Elemente-Methode (3)
- Rissausbreitung (3)
- Bruch (2)
Institute
Open Access
- Closed Access (16)
- Open Access (11)
- Closed (8)
- Gold (2)
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In this paper (Part I), the low-cycle fatigue (LCF) and TMF properties of HiSiMo are investigated in uniaxial tests and the damage mechanisms are addressed. On the basis of the experimental results a fatigue life model is developed which is based on elastic, plastic and creep fracture mechanics results of short cracks, so that time and temperature dependent effects on damage are taken into account. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper).
Hot forging dies are subjected to high cyclic thermo-mechanical loads. In critical areas, the occurring stresses can exceed the material’s yield limit. Additionally, loading at high temperatures leads to thermal softening of the used martensitic materials. These effects can result in an early crack initiation and unexpected failure of the dies, usually described as thermo-mechanical fatigue (TMF). In previous works, a temperature-dependent cyclic plasticity model for the martensitic hot forging tool steel 1.2367 (X38CrMoV5-3) was developed and implemented in the finite element (FE)-software Abaqus. However, in the forging industry, application-specific software is usually used to ensure cost-efficient numerical process design. Therefore, a new implementation for the FE-software Simufact Forming 16.0 is presented in this work. The results are compared and validated with the original implementation by means of a numerical compression test and a cyclic simulation is calculated with Simufact Forming.
Pure orbital blowout fractures occur within the confines of the internal orbital wall. Restoration of orbital form and volume is paramount to prevent functional and esthetic impairment. The anatomical peculiarity of the orbit has encouraged surgeons to develop implants with customized features to restore its architecture. This has resulted in worldwide clinical demand for patient-specific implants (PSIs) designed to fit precisely in the patient’s unique anatomy. Material extrusion or Fused filament fabrication (FFF) three-dimensional (3D) printing technology has enabled the fabrication of implant-grade polymers such as Polyetheretherketone (PEEK), paving the way for a more sophisticated generation of biomaterials. This study evaluates the FFF 3D printed PEEK orbital mesh customized implants with a metric considering the relevant design, biomechanical, and morphological parameters. The performance of the implants is studied as a function of varying thicknesses and porous design constructs through a finite element (FE) based computational model and a decision matrix based statistical approach. The maximum stress values achieved in our results predict the high durability of the implants, and the maximum deformation values were under one-tenth of a millimeter (mm) domain in all the implant profile configurations. The circular patterned implant (0.9 mm) had the best performance score. The study demonstrates that compounding multi-design computational analysis with 3D printing can be beneficial for the optimal restoration of the orbital floor.
Cast iron materials are used as materials for cylinder heads for heavy duty internal combustion engines. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. While high-cycle fatigue (HCF) is dominant for the material in the water jacket region, the combination of thermal transients with mechanical load cycles results in thermomechanical fatigue (TMF) of the material in the fire deck region, even including superimposed TMF and HCF loads. Increasing the efficiency of the engines directly leads to increasing combustion pressure and temperature and, thus, lower safety margins for the currently used cast iron materials or alternatively the need for superior cast iron materials. In this paper (Part I), the TMF properties of the lamellar graphite cast iron GJL250 and the vermicular graphite cast iron GJV450 are characterized in uniaxial tests and a mechanism-based model for TMF life prediction is developed for both materials. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper) and supports engineers in finding the appropriate material and design. Furthermore, the effect of the elastic, plastic and creep properties of the materials on the fatigue life can be evaluated with the model. However, for a material selection also the thermophysical properties, controlling to a high level the thermal stresses in the component, must be considered. Hence, the need for integral concepts for material characterization and selection from a multitude of existing and soon-to-be developed cast iron materials is discussed.
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their life cycle. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In Part I of the paper, a fracture mechanics model for TMF life prediction was developed based on results of uniaxial tests. In this paper (Part II), the model is formulated for three-dimensional stress states, so that it can be applied in a post-processing step of a finite-element analysis. To obtain reliable stresses and (time dependent plastic) strains in the finite-element calculation, a time and temperature dependent plasticity model is applied which takes non-linear kinematic hardening into account. The material properties of the model are identified from the results of the uniaxial test. The plasticity model and the TMF life model are applied to assess the lifetime of an exhaust manifold.
Cast aluminum alloys are frequently used as materials for cylinder head applications in internal combustion gasoline engines. These components must withstand severe cyclic mechanical and thermal loads throughout their lifetime. Reliable computational methods allow for accurate estimation of stresses, strains, and temperature fields and lead to more realistic Thermomechanical Fatigue (TMF) lifetime predictions. With accurate numerical methods, the components could be optimized via computer simulations and the number of required bench tests could be reduced significantly. These types of alloys are normally optimized for peak hardness from a quenched state that maximizes the strength of the material. However due to high temperature exposure, in service or under test conditions, the material would experience an over-ageing effect that leads to a significant reduction in the strength of the material. To numerically account for ageing effects, the Shercliff & Ashby ageing model is combined with a Chaboche-type viscoplasticity model available in the finite-element program ABAQUS by defining field variables. The constitutive model with ageing effects is correlated with uniaxial cyclic isothermal tests in the T6 state, the overaged state, as well as thermomechanical tests. On the other hand, the mechanism-based TMF damage model (DTMF) is calibrated for both T6 and over-aged state. Both the constitutive and the damage model are applied to a cylinder head component simulating several cycles on an engine dynamometer test. The effects of including ageing for both models are shown.
In this work, time-independent and time-dependent plasticity models are presented that are well suited for the calculation of stresses and strains with the finite-element method to assess the low-cycle and thermomechanical fatigue life of engineering components. The focus are plasticity models that are available in finite-element programs nowadays as standard material models and describe isotropic and kinematic hardening, strain-rate dependency as well as static recovery of hardening. For the presented models, aspects relevant for the application of the models are addressed as the determination of the material properties and the numerical implementation. Nevertheless, the plasticity models are also embedded in the thermodynamic framework used for the derivation of thermodynamically consistent plasticity models. Only uniaxial formulations are used to achieve a good readability and preventing the use of tensors.
The following contribution deals with the growth of cracks in low-cycle fatigue (LCF) and thermomechanical fatigue (TMF) tested specimens of Inconel 718 measured by using the replica method. The specimens are loaded with different strain rates. The material shows a significantly higher crack growth rate if the strain rate is decreased. Electron backscatter diffraction (EBSD) is adopted to identify the failure mechanism and the misorientation relationship of failed grain boundaries in secondary cracks. The analyzed cracks propagated mainly transgranular but also intergranular failure can be observed in some areas. It is found that grain boundaries with coincidence site lattice (CSL) boundary structure are generally less susceptible for intergranular failure than grain boundaries with random misorientation. For modeling the experimentally identified crack behavior an existing model for fatigue crack growth based on the mechanism of time dependent elastic–plastic crack tip blunting is enhanced to describe environmental effects based on the mechanism of oxygen diffusion at the crack tip. For the diffusion process the temperature dependent parabolic diffusion law is assumed. As a result, the time dependent cyclic crack tip opening displacement (DCTOD) is used as representative value to describe both mechanisms. Thus, most
of the included model parameters characterize the deformation behavior of the material and can be determined by independent material tests. With the determined material properties, the proposed model describes the experimentally measured crack growth curves very well. The model is validated based on predictions of the number of cycles to failure of LCF as well as in-phase and out-of-phase TMF tests in the temperature range between room temperature and 650 °C.
In this paper, a temperature-dependent viscoplasticity model is presented that describes thermal and cyclic softening of the hot work steel X38CrMoV5-3 under thermomechanical fatigue loading. The model describes the softening state of the material by evolution equations, the material properties of which can be determined on the basis of a defined experimental program. A kinetic model is employed to capture the effect of coarsening carbides and a new isotropic cyclic softening model is developed that takes history effects during thermomechanical loadings into account. The temperature-dependent material properties of the viscoplasticity model are determined on the basis of experimental data measured in isothermal and thermomechanical fatigue tests for the material X38CrMoV5-3 in the temperature range between 20 and 650 ∘C. The comparison of the model and an existing model for isotropic softening shows an improved description of the softening behavior under thermomechanical fatigue loading. A good overall description of the experimental data is possible with the presented viscoplasticity model, so that it is suited for the assessment of operating loads of hot forging tools.
In this paper, the Bauschinger effect and latent hardening of single crystals are assessed in finite element calculations using a single crystal plasticity model with kinematic hardening. To this end, results of cyclic micro-bending experiments on single crystal Alloy 718 in different crystal orientations (single slip and multi slip) with respect to the loading direction are used to determine the slip system related material properties of the single crystal plasticity model. Two kinematic hardening laws are considered: a kinematic hardening law describing latent hardening and a kinematic hardening law without latent hardening. For the determination of material properties for both hardening laws, a gradient-based optimization method is used. The results show that the different strength levels observed for micro-bending tests on different crystal orientations can only be described with latent kinematic hardening well, whereas the pronounced Bauschinger effect is described well by both kinematic hardening laws. It is concluded that cyclic micro-bending experiments on single crystals using different crystal orientations give an appropriate data base for the determination of the slip system related material properties of the single crystal plasticity model with latent kinematic hardening.