Turbocharger housings in internal combustion engines are subjected to severe mechanical and thermal cyclic loads throughout their life-time or during engine testing. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermo-mechanical fatigue (TMF) of the material. For the computational TMF life assessment of high temperature components, the DTMF model can provide reliable TMF life predictions. The model is based on a short fatigue crack growth law and uses local finite-element (FE) results to predict the number of cycles to failure for a technical crack. In engine applications, it is nowadays often acceptable to have short cracks as long as they do not propagate and cause loss of function of the component. Thus, it is necessary to predict not only potential crack locations and the corresponding number of cycles for a technical crack, but also to determine subsequent crack growth or even a possible crack arrest. In this work, a method is proposed that allows the simulation of TMF crack growth in high temperature components using FE simulations and non-linear fracture mechanics (NLFM).
A NLFM based crack growth simulation method is described. This method starts with the FE analysis of a component. In this paper, the method is demonstrated for an automotive turbocharger housing subjected to TMF loading. A transient elastic-viscoplastic FE analysis is used to simulate four heating and cooling cycles of an engine test. The stresses, inelastic strains, and temperature histories from the FEA are then used to perform TMF life predictions using the standard DTMF model. The crack position and the crack plane of critical hotspots are then identified. Simulated cracks are inserted at the hotspots. For the model demonstrated, cracks were inserted at two hotspot locations. The ΔJ integral is computed as a fracture mechanics parameter at each point along the crack-front, and the crack extension of each point is then evaluated, allowing the crack to grow iteratively. The paper concludes with a comparison of the crack growth curves for both hotspots with experimental results.
Cast aluminum cylinder blocks are frequently used in gasoline and diesel internal combustion engines because of their light-weight advantage. However, the disadvantage of aluminum alloys is their relatively low strength and fatigue resistance which make aluminum blocks prone to fatigue cracking. Engine blocks must withstand a combination of low-cycle fatigue (LCF) thermal loads and high-cycle fatigue (HCF) combustion and dynamic loads. Reliable computational methods are needed that allow for accurate fatigue assessment of cylinder blocks under this combined loading. In several publications, the mechanism-based thermomechanical fatigue (TMF) damage model DTMF describing the growth of short fatigue cracks has been extended to include the effect of both LCF thermal loads and superimposed HCF loadings. This approach is applied to the finite life fatigue assessment of an aluminum cylinder block. The required material properties related to LCF are determined from uniaxial LCF tests. The additional material properties required for the assessment of superimposed HCF are obtained from the literature for similar materials. The predictions of the model agree well with engine dyno test results. Finally, some improvements to the current process are discussed.
In this paper a practical way for fatigue life prediction of rubber products under multiaxial loads is shown. This is done by means of fracture mechanical concepts and the energy release rate as the failure criterion. Due to a FEA post-processor the potential energy release rate might be calculated at every material point supposed there was a crack. And therefore the risk of failure and with the help of a strain number curve the time to fatigue is able to be calculated by FEA. This concept is applied for an estimation of the life time of a test specimen with tensile loading from fatigue data of a shear loaded specimen of different design. This rather more theoretical concept of the energy release rate is complemented by experimental crack growth data by a Tear Fatigue Analyzer with its great advantage of reduction of testing time and costs compared to those of fatigue tests. For some materials a thorough characterization of crack growth and fatigue behavior is presented and is applied to estimate the time to fatigue by FEA for a real component under multiaxial loads.
The following contribution deals with the growth of cracks in low-cycle fatigue (LCF) and thermomechanical fatigue (TMF) tested specimens of Inconel 718 measured by using the replica method. The specimens are loaded with different strain rates. The material shows a significantly higher crack growth rate if the strain rate is decreased. Electron backscatter diffraction (EBSD) is adopted to identify the failure mechanism and the misorientation relationship of failed grain boundaries in secondary cracks. The analyzed cracks propagated mainly transgranular but also intergranular failure can be observed in some areas. It is found that grain boundaries with coincidence site lattice (CSL) boundary structure are generally less susceptible for intergranular failure than grain boundaries with random misorientation. For modeling the experimentally identified crack behavior an existing model for fatigue crack growth based on the mechanism of time dependent elastic–plastic crack tip blunting is enhanced to describe environmental effects based on the mechanism of oxygen diffusion at the crack tip. For the diffusion process the temperature dependent parabolic diffusion law is assumed. As a result, the time dependent cyclic crack tip opening displacement (DCTOD) is used as representative value to describe both mechanisms. Thus, most
of the included model parameters characterize the deformation behavior of the material and can be determined by independent material tests. With the determined material properties, the proposed model describes the experimentally measured crack growth curves very well. The model is validated based on predictions of the number of cycles to failure of LCF as well as in-phase and out-of-phase TMF tests in the temperature range between room temperature and 650 °C.