Pure gas adsorption isotherms of CH4 and N2 and their binary mixtures were measured at 273 K, 298 K and 323 K and up to 2 MPa on two different microporous metal–organic frameworks (MOFs), i.e. the commercially available Basolite® A100 and the recently reported copper-based triazolyl benzoate MOF 3∞[Cu(Me-4py-trz-ia)] (1). The Tòth isotherm model and the vacancy solution model were used to describe the experimentally determined isotherms and proved to be well suited for this purpose. While 1 shows a more homogeneous surface with a nearly constant isosteric heat of adsorption of 18–18.5 kJ mol−1 for CH4 and 12–15 kJ mol−1 for N2, the isosteric heat of adsorption at zero coverage for Basolite® A100 is 19 kJ mol−1 for CH4 and 16.2 kJ mol−1 for N2, decreasing significantly with increasing loading. Binary adsorption isotherms were measured gravimetrically to determine the total adsorbed mass of CH4 and N2. The van Ness method was successfully applied to calculate partial loadings from gravimetrically measured binary adsorption isotherms. Further studies by volumetric–chromatographic experiments support the good correlation between experimental data and predictions by the vacancy solution model (VSM-Wilson) and the ideal adsorbed solution theory (IAST) from pure gas isotherms. The experimental selectivities were determined to be αCH4/N2 = 4.0–5.0 for 1, slightly higher than for Basolite® A100 with αCH4/N2 = 3.4–4.5. These values are in good agreement with predictions for ideal selectivities based on Henry's law constants. From the experimental selectivities the potential of both MOFs in gas separation of CH4 from N2 can be derived.
Synthesis and crystal structure of a novel copper-based MOF material are presented. The tetragonal crystal structure of [ ∞ 3 ( Cu 4 ( μ 4 -O ) ( μ 2 -OH ) 2 ( Me 2 trz p ba ) 4 ] possesses a calculated solvent-accessible pore volume of 57%. Besides the preparation of single crystals, synthesis routes to microcrystalline materials are reported. While PXRD measurements ensure the phase purity of the as-synthesized material, TD-PXRD measurements and coupled DTA–TG–MS analysis confirm the stability of the network up to 230 °C. The pore volume of the microcrystalline material determined by nitrogen adsorption at 77 K depends on the synthetic conditions applied. After synthesis in DMF/H2O/MeOH the pores are blocked for nitrogen, whereas they are accessible for nitrogen after synthesis in H2O/EtOH and subsequent MeOH Soxhleth extraction. The corresponding experimental pore volume was determined by nitrogen adsorption to be V Pore = 0.58 cm 3 g - 1 . In order to characterize the new material and to show its adsorption potential, comprehensive adsorption studies with different adsorptives such as nitrogen, argon, carbon dioxide, methanol and methane at different temperatures were carried out. Unusual adsorption–desorption isotherms with one or two hysteresis loops are found – a remarkable feature of the new flexible MOF material.
Uptakes of 9.2 mmol g−1 (40.5 wt %) for CO2 at 273 K/0.1 MPa and 15.23 mmol g−1 (3.07 wt %) for H2 at 77 K/0.1 MPa are among the highest reported for metal–organic frameworks (MOFs) and are found for a novel, highly microporous copper‐based MOF (see picture; Cu turquoise, O red, N blue). Thermal analyses show a stability of the flexible framework up to 250 °C.
Metal–organic frameworks (MOFs) as highly porous materials have gained increasing interest because of their distinct adsorption properties.1–3 They exhibit a high potential for applications in gas separation and storage,4 as sensors5 as well as in heterogeneous catalysis.6 In the last few years, the H2 storage capacity of MOFs has been considerably increased. Mesoporous MOFs show high adsorption capacities for CH4, CO2, and H2 at high pressures.2, 3, 7–10 To increase the uptake of H2 and CO2 by physisorption at ambient pressure, adsorbents with small micropores as well as high specific surface areas and micropore volumes are required.11, 12 Such microporous materials seem to be more appropriate for gas‐mixture separation by physisorption than mesoporous materials. For gas separation in MOFs the interactions between the fluid adsorptive and “open metal sites” (coordinatively unsaturated binding sites) or the ligands are regarded as important.13 Industrial processes, such as natural‐gas purification or biogas upgrading, can be improved with those materials during a vapor‐pressure swing adsorption cycle (VPSA cycle) or a temperature swing adsorption cycle (TSA cycle).14 The microporous MOF series CPO‐27‐M (M=Mg, Co, Ni, Zn), for example, shows very high CO2 uptakes at low pressures (<0.1 MPa).15, 16 Concerning H2 adsorption, the microporous MOF PCN‐12 offers with 3.05 wt % the highest uptake at ambient pressure and 77 K reported to date.17
Herein, we present a novel microporous copper‐based MOF equation image[Cu(Me‐4py‐trz‐ia)] (1; Me‐4py‐trz‐ia2−=5‐(3‐methyl‐5‐(pyridin‐4‐yl)‐4H‐1,2,4‐triazol‐4‐yl)isophthalate) with extraordinarily high CO2 and H2 uptakes at ambient pressure, the H2 uptake being similar to that in PCN‐12. The ligand Me‐4py‐trz‐ia2−, which can be obtained from cheap starting materials by a three‐step synthesis in good yield, combines carboxylate, triazole, and pyridine functions and is adopted from a recently presented series of linkers,18 for which up to now only a few coordination polymers are known.