Refine
Year of publication
Document Type
- Article (reviewed) (28) (remove)
Is part of the Bibliography
- yes (28)
Keywords
- Ermüdung (8)
- Plastizität (8)
- Mikrostruktur (5)
- Eisenguss (4)
- Finite-Elemente-Methode (3)
- Materialermüdung (3)
- Simulation (3)
- Thermomechanik (3)
- Bruch (2)
- Crack opening stress (2)
Institute
Open Access
- Closed Access (12)
- Open Access (9)
- Closed (3)
- Gold (2)
In this paper, the J-integral is derived for temperature-dependent elastic–plastic materials described by incremental plasticity. It is implemented using the equivalent domain integral method for assessment of three-dimensional cracks based on results of finite-element calculations. The J-integral considers contributions from inhomogeneous temperature fields and temperature-dependent elastic and plastic material properties as well as from gradients in the plastic strains and the hardening variables. Different energy densities are considered, the Helmholtz free energy and the stress-working density, providing a physical meaning of the J-integral as a fracture criteria for crack growth. Results obtained for a plate with two different crack configurations each loaded by a cool-down thermal shock show domain-independence of the incremental J-integral for different energy densities even for high temperature gradients and significant temperature-dependence of the yield stress and the hardening exponent in the presence of large scale yielding. Hence, the derived J-integral is an appropriate parameter for the assessment of cracks in thermomechanically loaded components.
In this paper, the temperature dependent cyclic mechanical properties of the martensitic hot work tool steel 1.2367 after tempering are investigated. To this end, hardness measurements as well as monotonic and cyclic tests at temperatures in the range from room temperature to 650 °C are performed on material tempered for different tempering times and temperatures. To describe the observed time and temperature dependent softening during tempering a kinetic model for the evolution of the mean size of secondary carbides based on Ostwald ripening is developed. Furthermore, mechanism-based as well as phenomenological relations for the cyclic mechanical properties of the Ramberg-Osgood model depending on carbide size and temperature are introduced. A good overall agreement of the measured and the calculated stress-strain hysteresis loops for different temperatures and heat treatments is obtained using the determined material properties of the kinetic and mechanical model.
In this paper, an unconditionally stable algorithm for the numerical integration and finite-element implementation of a class of pressure dependent plasticity models with nonlinear isotropic and kinematic hardening is presented. Existing algorithms are improved in the sense that the number of equations to be solved iteratively is significantly reduced. This is achieved by exploitation of the structure of Armstrong-Frederik-type kinematic hardening laws. The consistent material tangent is derived analytically and compared to the numerically computed tangent in order to validate the implementation. The performance of the new algorithm is compared to an existing one that does not consider the possibility of reducing the number of unknowns to be iterated. The algorithm is used to implement a time and temperature dependent cast iron plasticity model, which is based on the pressure dependent Gurson model, in the finite-element program ABAQUS. The implementation is applied to compute stresses and strains in a large-scale finite-element model of a three cylinder engine block. This computation proofs the applicability of the algorithm in industrial practice that is of interest in applied sciences.
Due to higher combustion chamber temperatures and pressures in efficient combustion engines, both the high-cycle and thermomechanical fatigue loads on service life-critical components, such as the cylinder head, are increasing. Material comparisons and analysis of damage behavior are very expensive and time-consuming using component tests. This study therefore develops a test method for cylinder head materials that takes into account the combined loading conditions from the above-mentioned loads and allows realistic temperature transients and gradients on near-component samples. The near-component cylinder head sample represents the failure-critical exhaust valve crosspiece and is tested in a test rig specially designed with the aid of conjugate heat transfer simulations. In the test rig, the sample is subjected to thermal stress by a hot gas burner and to mechanical stress by a high-frequency pulsator. Optical crack detection allows permanent observation of fatigue crack growth and crack closure during the test. Fractographic and metallo-graphic examinations of the fracture areas as well as analyses of the damage patterns show that loads close to engine operation can be set in this way and their influences on the damage can be monitored.
In this paper, the effect of the polycrystalline microstructure on crack-tip opening displacement and crack closure is investigated for microstructural short plane strain fatigue cracks using the finite-element method. To this end, cracks are introduced in synthetically generated microstructures and the grain properties are described using a single crystal plasticity model with kinematic hardening. Additionally, finite-element calculations without resolved microstructure and von Mises plasticity with kinematic hardening are performed. Fully-reversed strain-controlled cyclic loadings are considered under large-scale yielding conditions as typical for low-cycle fatigue problems. The crack opening stress and the cyclic crack-tip opening displacement are significantly influenced by the local grain structure. While the stabilized crack opening stresses obtained with the microstructure-based finite-element model are in good accordance with the von Mises plasticity results, the differences in the cyclic crack opening displacement are addressed to the asymmetric plastic strain fields in the plastic wake behind the crack-tip of the microstructure-based model. The asymmetric plastic strain fields result in discontinuous and premature contact of the crack flanks.
In dem abgeschlossenen Vorhaben „Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Motorbauteilen unter thermisch-mechanischer Ermüdungsbeanspruchung“ der Forschungsvereinigung Verbrennungskraftmaschinen e. V. (FVV) wurde am Fraunhofer Institut für Werkstoffmechanik IWM in Freiburg ein Materialmodell zur Lebensdauervorhersage thermomechanisch belasteter Komponenten entwickelt. Das Modell basiert auf einem viskoplastischen Verformungsmodell für Eisengusswerkstoffe und einem mechanismenbasierten Modell für Mikrorisswachstum zur Lebensdauervorhersage.
This paper reports on the evolution of cracks in the cylinder heads of a large V8 Diesel engine during cyclic engine tests. The observations are compared with the predictions of a lifetime model for combined thermo-mechanical (TMF) and high cycle fatigue (HCF) loading, which is based on a fracture mechanics analysis of microcrack growth in viscoplastic solids and assumes that the crack advance per cycle is proportional to the cyclic crack tip opening displacement. Since the material of the cylinder heads, the cast iron EN-GJV450, exhibits the typical features of cast iron, namely pressure dependence of the yield stress, dilatancy and tension-compression asymmetry, the Gurson model is applied and combined with the viscoplastic Chaboche model. This constitutive model together with the lifetime model is implemented into a finite element code as a user defined material routine. Published model parameters for the considered cast iron are used to carry out the simulation of the engine test. This simulation comprises a CFD analysis to determine the heat transfer coefficients, a thermal analysis of the load cycle and the mechanical analysis. The thermal analysis reproduces the temperatures at various measuring points sufficiently accurately. Finally, the mechanical analysis predicts the location and orientation of the cracks in the valve bridges correctly in all cases. However, the lifetime predictions are rather conservative compared to the tests (by a factor of 1 to 5 in lifetime). This is discussed and explained by the fact that the cracks were detected in the tests only when they had already spread over a substantial fraction of the valve bridge width. To describe this situation a long-crack analysis would be necessary, which is not yet included in the applied lifetime model.
A complete thermomechanical fatigue (TMF) life prediction methodology is developed for predicting the TMF life of cast iron cylinder heads for efficient heavy duty internal combustion engines. The methodology uses transient temperature fields as thermal loads for the non-linear structural finite-element analysis (FEA). To obtain reliable stress and strain histories in the FEA for cast iron materials, a time and temperature dependent plasticity model which accounts for viscous effects, non-linear kinematic hardening and tensioncompression asymmetry is required. For this purpose a unified elasto-viscoplastic Chaboche model coupled with damage is developed and implemented as a user material model (USERMAT) in the general purpose FEA program ANSYS. In addition, the mechanismbased DTMF model for TMF life prediction developed in Part I of the paper is extended to three-dimensional stress states under transient non-proportional loading conditions. The material properties of the plasticity model are determined for lamellar graphite cast iron GJL250 and vermicular graphite cast iron GJV450 from isothermal and non-isothermal uniaxial tests. The methodology is applied to obtain a TMF life prediction on two cast iron cylinder heads for heavy duty diesel engine applications made from both cast iron materials. It is shown that the life predictions using the developed methodology correlate very well with observed lives from two bench tests in terms of location as well as number of cycles to failure.
Cast iron materials are used as materials for cylinder heads for heavy duty internal combustion engines. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. While high-cycle fatigue (HCF) is dominant for the material in the water jacket region, the combination of thermal transients with mechanical load cycles results in thermomechanical fatigue (TMF) of the material in the fire deck region, even including superimposed TMF and HCF loads. Increasing the efficiency of the engines directly leads to increasing combustion pressure and temperature and, thus, lower safety margins for the currently used cast iron materials or alternatively the need for superior cast iron materials. In this paper (Part I), the TMF properties of the lamellar graphite cast iron GJL250 and the vermicular graphite cast iron GJV450 are characterized in uniaxial tests and a mechanism-based model for TMF life prediction is developed for both materials. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper) and supports engineers in finding the appropriate material and design. Furthermore, the effect of the elastic, plastic and creep properties of the materials on the fatigue life can be evaluated with the model. However, for a material selection also the thermophysical properties, controlling to a high level the thermal stresses in the component, must be considered. Hence, the need for integral concepts for material characterization and selection from a multitude of existing and soon-to-be developed cast iron materials is discussed.
In this paper, the time- and temperature-dependent cyclic ratchetting plasticity of the nickel-based alloy IN100 is experimentally investigated in strain-controlled experiments in the temperature range from 300 °C to 1050 °C. To this end, uniaxial material tests are performed with complex loading histories designed to activate phenomena as strain rate dependency, stress relaxation as well as the Bauschinger effect, cyclic hardening and softening, ratchetting and recovery from hardening. Plasticity models with different levels of complexity are presented that consider these phenomena, and a strategy is derived to determine the multitude of temperature-dependent material properties of the models in a step-by-step procedure based on sub-sets of experimental data of isothermal experiments. The models and the material properties are validated based on the results of non-isothermal experiments. A good description of the time- and temperature-dependent cyclic ratchetting plasticity of IN100 is obtained for isothermal as well as non-isothermal loading with models including ratchetting terms in the kinematic hardening law and the material properties obtained with the proposed strategy.