Turbocharger housings in internal combustion engines are subjected to severe mechanical and thermal cyclic loads throughout their life-time or during engine testing. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermo-mechanical fatigue (TMF) of the material. For the computational TMF life assessment of high temperature components, the DTMF model can provide reliable TMF life predictions. The model is based on a short fatigue crack growth law and uses local finite-element (FE) results to predict the number of cycles to failure for a technical crack. In engine applications, it is nowadays often acceptable to have short cracks as long as they do not propagate and cause loss of function of the component. Thus, it is necessary to predict not only potential crack locations and the corresponding number of cycles for a technical crack, but also to determine subsequent crack growth or even a possible crack arrest. In this work, a method is proposed that allows the simulation of TMF crack growth in high temperature components using FE simulations and non-linear fracture mechanics (NLFM).
A NLFM based crack growth simulation method is described. This method starts with the FE analysis of a component. In this paper, the method is demonstrated for an automotive turbocharger housing subjected to TMF loading. A transient elastic-viscoplastic FE analysis is used to simulate four heating and cooling cycles of an engine test. The stresses, inelastic strains, and temperature histories from the FEA are then used to perform TMF life predictions using the standard DTMF model. The crack position and the crack plane of critical hotspots are then identified. Simulated cracks are inserted at the hotspots. For the model demonstrated, cracks were inserted at two hotspot locations. The ΔJ integral is computed as a fracture mechanics parameter at each point along the crack-front, and the crack extension of each point is then evaluated, allowing the crack to grow iteratively. The paper concludes with a comparison of the crack growth curves for both hotspots with experimental results.
Cast aluminum cylinder blocks are frequently used in gasoline and diesel internal combustion engines because of their light-weight advantage. However, the disadvantage of aluminum alloys is their relatively low strength and fatigue resistance which make aluminum blocks prone to fatigue cracking. Engine blocks must withstand a combination of low-cycle fatigue (LCF) thermal loads and high-cycle fatigue (HCF) combustion and dynamic loads. Reliable computational methods are needed that allow for accurate fatigue assessment of cylinder blocks under this combined loading. In several publications, the mechanism-based thermomechanical fatigue (TMF) damage model DTMF describing the growth of short fatigue cracks has been extended to include the effect of both LCF thermal loads and superimposed HCF loadings. This approach is applied to the finite life fatigue assessment of an aluminum cylinder block. The required material properties related to LCF are determined from uniaxial LCF tests. The additional material properties required for the assessment of superimposed HCF are obtained from the literature for similar materials. The predictions of the model agree well with engine dyno test results. Finally, some improvements to the current process are discussed.
High temperature components in internal combustion engines and exhaust systems must withstand severe mechanical and thermal cyclic loads throughout their lifetime. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material. Analytical tools are increasingly employed by designers and engineers for component durability assessment well before any hardware testing. The DTMF model for TMF life prediction, which assumes that micro-crack growth is the dominant damage mechanism, is capable of providing reliable predictions for a wide range of high-temperature components and materials in internal combustion engines. Thus far, the DTMF model has employed a local approach where surface stresses, strains, and temperatures are used to compute damage for estimating the number of cycles for a small initial defect or micro-crack to reach a critical length. In the presence of significant gradients of stresses, strains, and temperatures, the use of surface field values could lead to very conservative estimates of TMF life when compared with reported lives from hardware testing. As an approximation of gradient effects, a non-local approach of the DTMF model is applied. This approach considers through-thickness fields where the micro-crack growth law is integrated through the thickness considering these variable fields. With the help of software tools, this method is automated and applied to components with complex geometries and fields. It is shown, for the TMF life prediction of a turbocharger housing, that the gradient correction using the non-local approach leads to more realistic life predictions and can distinguish between surface cracks that may arrest or propagate through the thickness and lead to component failure.
Cast aluminum alloys are frequently used as materials for cylinder head applications in internal combustion gasoline engines. These components must withstand severe cyclic mechanical and thermal loads throughout their lifetime. Reliable computational methods allow for accurate estimation of stresses, strains, and temperature fields and lead to more realistic Thermomechanical Fatigue (TMF) lifetime predictions. With accurate numerical methods, the components could be optimized via computer simulations and the number of required bench tests could be reduced significantly. These types of alloys are normally optimized for peak hardness from a quenched state that maximizes the strength of the material. However due to high temperature exposure, in service or under test conditions, the material would experience an over-ageing effect that leads to a significant reduction in the strength of the material. To numerically account for ageing effects, the Shercliff & Ashby ageing model is combined with a Chaboche-type viscoplasticity model available in the finite-element program ABAQUS by defining field variables. The constitutive model with ageing effects is correlated with uniaxial cyclic isothermal tests in the T6 state, the overaged state, as well as thermomechanical tests. On the other hand, the mechanism-based TMF damage model (DTMF) is calibrated for both T6 and over-aged state. Both the constitutive and the damage model are applied to a cylinder head component simulating several cycles on an engine dynamometer test. The effects of including ageing for both models are shown.