600 Technik, Medizin, angewandte Wissenschaften
Refine
Document Type
- Article (reviewed) (12)
- Conference Proceeding (4)
Conference Type
- Konferenzartikel (4)
Is part of the Bibliography
- yes (16)
Keywords
- Plastizität (9)
- Materialermüdung (5)
- Ermüdung (4)
- Mikrostruktur (4)
- Eisenguss (3)
- Rissausbreitung (3)
- Simulation (3)
- Festigkeit (2)
- Microstructure (2)
- Stahl (2)
Institute
Open Access
- Closed (5)
- Closed Access (4)
- Open Access (3)
- Gold (2)
Turbocharger housings in internal combustion engines are subjected to severe mechanical and thermal cyclic loads throughout their life-time or during engine testing. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermo-mechanical fatigue (TMF) of the material. For the computational TMF life assessment of high temperature components, the DTMF model can provide reliable TMF life predictions. The model is based on a short fatigue crack growth law and uses local finite-element (FE) results to predict the number of cycles to failure for a technical crack. In engine applications, it is nowadays often acceptable to have short cracks as long as they do not propagate and cause loss of function of the component. Thus, it is necessary to predict not only potential crack locations and the corresponding number of cycles for a technical crack, but also to determine subsequent crack growth or even a possible crack arrest. In this work, a method is proposed that allows the simulation of TMF crack growth in high temperature components using FE simulations and non-linear fracture mechanics (NLFM).
A NLFM based crack growth simulation method is described. This method starts with the FE analysis of a component. In this paper, the method is demonstrated for an automotive turbocharger housing subjected to TMF loading. A transient elastic-viscoplastic FE analysis is used to simulate four heating and cooling cycles of an engine test. The stresses, inelastic strains, and temperature histories from the FEA are then used to perform TMF life predictions using the standard DTMF model. The crack position and the crack plane of critical hotspots are then identified. Simulated cracks are inserted at the hotspots. For the model demonstrated, cracks were inserted at two hotspot locations. The ΔJ integral is computed as a fracture mechanics parameter at each point along the crack-front, and the crack extension of each point is then evaluated, allowing the crack to grow iteratively. The paper concludes with a comparison of the crack growth curves for both hotspots with experimental results.
Cast aluminum cylinder blocks are frequently used in gasoline and diesel internal combustion engines because of their light-weight advantage. However, the disadvantage of aluminum alloys is their relatively low strength and fatigue resistance which make aluminum blocks prone to fatigue cracking. Engine blocks must withstand a combination of low-cycle fatigue (LCF) thermal loads and high-cycle fatigue (HCF) combustion and dynamic loads. Reliable computational methods are needed that allow for accurate fatigue assessment of cylinder blocks under this combined loading. In several publications, the mechanism-based thermomechanical fatigue (TMF) damage model DTMF describing the growth of short fatigue cracks has been extended to include the effect of both LCF thermal loads and superimposed HCF loadings. This approach is applied to the finite life fatigue assessment of an aluminum cylinder block. The required material properties related to LCF are determined from uniaxial LCF tests. The additional material properties required for the assessment of superimposed HCF are obtained from the literature for similar materials. The predictions of the model agree well with engine dyno test results. Finally, some improvements to the current process are discussed.
In this paper, the J-integral is derived for temperature-dependent elastic–plastic materials described by incremental plasticity. It is implemented using the equivalent domain integral method for assessment of three-dimensional cracks based on results of finite-element calculations. The J-integral considers contributions from inhomogeneous temperature fields and temperature-dependent elastic and plastic material properties as well as from gradients in the plastic strains and the hardening variables. Different energy densities are considered, the Helmholtz free energy and the stress-working density, providing a physical meaning of the J-integral as a fracture criteria for crack growth. Results obtained for a plate with two different crack configurations each loaded by a cool-down thermal shock show domain-independence of the incremental J-integral for different energy densities even for high temperature gradients and significant temperature-dependence of the yield stress and the hardening exponent in the presence of large scale yielding. Hence, the derived J-integral is an appropriate parameter for the assessment of cracks in thermomechanically loaded components.
In this paper, the time- and temperature-dependent cyclic ratchetting plasticity of the nickel-based alloy IN100 is experimentally investigated in strain-controlled experiments in the temperature range from 300 °C to 1050 °C. To this end, uniaxial material tests are performed with complex loading histories designed to activate phenomena as strain rate dependency, stress relaxation as well as the Bauschinger effect, cyclic hardening and softening, ratchetting and recovery from hardening. Plasticity models with different levels of complexity are presented that consider these phenomena, and a strategy is derived to determine the multitude of temperature-dependent material properties of the models in a step-by-step procedure based on sub-sets of experimental data of isothermal experiments. The models and the material properties are validated based on the results of non-isothermal experiments. A good description of the time- and temperature-dependent cyclic ratchetting plasticity of IN100 is obtained for isothermal as well as non-isothermal loading with models including ratchetting terms in the kinematic hardening law and the material properties obtained with the proposed strategy.
Hot forging dies are subjected to high cyclic thermo-mechanical loads. In critical areas, the occurring stresses can exceed the material’s yield limit. Additionally, loading at high temperatures leads to thermal softening of the used martensitic materials. These effects can result in an early crack initiation and unexpected failure of the dies, usually described as thermo-mechanical fatigue (TMF). In previous works, a temperature-dependent cyclic plasticity model for the martensitic hot forging tool steel 1.2367 (X38CrMoV5-3) was developed and implemented in the finite element (FE)-software Abaqus. However, in the forging industry, application-specific software is usually used to ensure cost-efficient numerical process design. Therefore, a new implementation for the FE-software Simufact Forming 16.0 is presented in this work. The results are compared and validated with the original implementation by means of a numerical compression test and a cyclic simulation is calculated with Simufact Forming.
In this paper, a temperature-dependent viscoplasticity model is presented that describes thermal and cyclic softening of the hot work steel X38CrMoV5-3 under thermomechanical fatigue loading. The model describes the softening state of the material by evolution equations, the material properties of which can be determined on the basis of a defined experimental program. A kinetic model is employed to capture the effect of coarsening carbides and a new isotropic cyclic softening model is developed that takes history effects during thermomechanical loadings into account. The temperature-dependent material properties of the viscoplasticity model are determined on the basis of experimental data measured in isothermal and thermomechanical fatigue tests for the material X38CrMoV5-3 in the temperature range between 20 and 650 ∘C. The comparison of the model and an existing model for isotropic softening shows an improved description of the softening behavior under thermomechanical fatigue loading. A good overall description of the experimental data is possible with the presented viscoplasticity model, so that it is suited for the assessment of operating loads of hot forging tools.
In this paper, the effect of the polycrystalline microstructure on crack-tip opening displacement and crack closure is investigated for microstructural short plane strain fatigue cracks using the finite-element method. To this end, cracks are introduced in synthetically generated microstructures and the grain properties are described using a single crystal plasticity model with kinematic hardening. Additionally, finite-element calculations without resolved microstructure and von Mises plasticity with kinematic hardening are performed. Fully-reversed strain-controlled cyclic loadings are considered under large-scale yielding conditions as typical for low-cycle fatigue problems. The crack opening stress and the cyclic crack-tip opening displacement are significantly influenced by the local grain structure. While the stabilized crack opening stresses obtained with the microstructure-based finite-element model are in good accordance with the von Mises plasticity results, the differences in the cyclic crack opening displacement are addressed to the asymmetric plastic strain fields in the plastic wake behind the crack-tip of the microstructure-based model. The asymmetric plastic strain fields result in discontinuous and premature contact of the crack flanks.
Cast aluminum alloys are frequently used as materials for cylinder head applications in internal combustion gasoline engines. These components must withstand severe cyclic mechanical and thermal loads throughout their lifetime. Reliable computational methods allow for accurate estimation of stresses, strains, and temperature fields and lead to more realistic Thermomechanical Fatigue (TMF) lifetime predictions. With accurate numerical methods, the components could be optimized via computer simulations and the number of required bench tests could be reduced significantly. These types of alloys are normally optimized for peak hardness from a quenched state that maximizes the strength of the material. However due to high temperature exposure, in service or under test conditions, the material would experience an over-ageing effect that leads to a significant reduction in the strength of the material. To numerically account for ageing effects, the Shercliff & Ashby ageing model is combined with a Chaboche-type viscoplasticity model available in the finite-element program ABAQUS by defining field variables. The constitutive model with ageing effects is correlated with uniaxial cyclic isothermal tests in the T6 state, the overaged state, as well as thermomechanical tests. On the other hand, the mechanism-based TMF damage model (DTMF) is calibrated for both T6 and over-aged state. Both the constitutive and the damage model are applied to a cylinder head component simulating several cycles on an engine dynamometer test. The effects of including ageing for both models are shown.
High temperature components in internal combustion engines and exhaust systems must withstand severe mechanical and thermal cyclic loads throughout their lifetime. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material. Analytical tools are increasingly employed by designers and engineers for component durability assessment well before any hardware testing. The DTMF model for TMF life prediction, which assumes that micro-crack growth is the dominant damage mechanism, is capable of providing reliable predictions for a wide range of high-temperature components and materials in internal combustion engines. Thus far, the DTMF model has employed a local approach where surface stresses, strains, and temperatures are used to compute damage for estimating the number of cycles for a small initial defect or micro-crack to reach a critical length. In the presence of significant gradients of stresses, strains, and temperatures, the use of surface field values could lead to very conservative estimates of TMF life when compared with reported lives from hardware testing. As an approximation of gradient effects, a non-local approach of the DTMF model is applied. This approach considers through-thickness fields where the micro-crack growth law is integrated through the thickness considering these variable fields. With the help of software tools, this method is automated and applied to components with complex geometries and fields. It is shown, for the TMF life prediction of a turbocharger housing, that the gradient correction using the non-local approach leads to more realistic life predictions and can distinguish between surface cracks that may arrest or propagate through the thickness and lead to component failure.
Hot work tools are subjected to complex thermal and mechanical loads during hot forming processes. Locally, the stresses can exceed the material’s yield strength in highly loaded areas as e.g. in small radii in die cavities. To sustain the high loads, the hot forming tools are typically made of martensitic hot work steels. While temperatures for annealing of the tool steels usually lie in the range between 400 and 600 °C, the steels may experience even higher temperatures during hot forming, resulting in softening of the material due to coarsening of strengthening particles. In this paper, a temperature dependent cyclic plasticity model for the martensitic hot work tool steel 1.2367 (X38CrMoV5-3) is presented that includes softening due to particle coarsening and that can be applied in finite-element calculations to assess the effect of softening on the thermomechanical fatigue life of hot work tools. To this end, a kinetic model for the evolution of the mean size of secondary carbides based on Ostwald ripening is coupled with a cyclic plasticity model with kinematic hardening. Mechanism-based relations are developed to describe the dependency of the mechanical properties on carbide size and temperature. The material properties of the mechanical and kinetic model are determined on the basis of tempering hardness curves as well as monotonic and cyclic tests.