We present an electrochemical model of a lithium iron phosphate/graphite (LFP/C6) cell that includes combined aging mechanisms: (i) Electrochemical formation of the solid electrolyte interphase (SEI) at the anode, leading to loss of lithium inventory, (ii) breaking of the SEI due to volume changes of the graphite particles, causing accelerated SEI growth, and (iii) loss of active material due to of loss percolation of the liquid electrolyte resulting from electrode dry-out. The latter requires the introduction of an activity-saturation relationship. A time-upscaling methodology is developed that allows to simulate large time spans (thousands of operating hours). The combined modeling and simulation framework is able to predict calendaric and cyclic aging up to the end of life of the battery cells. The aging parameters are adjusted to match literature calendaric and cyclic aging experiments, resulting in quantitative agreement of simulated nonlinear capacity loss with experimental data. The model predicts and provides an interpretation for the dependence of capacity loss on temperature, cycling depth, and average SOC. The introduction of a percolation threshold in the activity-saturation relationship allows to capture the strong nonlinearity of aging toward end of life (“sudden death”).
Battery degradation is a complex physicochemical process that strongly depends on operating conditions and environment. We present a model-based analysis of lithium-ion battery degradation in smart microgrids, in particular, a single-family house and an office tract with photovoltaics generator. We use a multi-scale multi-physics model of a graphite/lithium iron phosphate (LiFePO4, LFP) cell including SEI formation as ageing mechanism. The cell-level model is dynamically coupled to a system-level model consisting of photovoltaics, inverter, power consumption profiles, grid interaction, and energy management system, fed with historic weather data. The behavior of the cell in terms of degradation propensity, performance, state of charge and other internal states is predicted over an annual operation cycle. As result, we have identified a peak in degradation rate during the battery charging process, caused by charging overpotentials. Ageing strongly depends on the load situation, where the predicted annual capacity fade is 1.9 % for the single-family house and only 1.3 % for the office tract.
Battery degradation is a complex physicochemical process that strongly depends on operating conditions. We present a model-based analysis of lithium-ion battery degradation in a stationary photovoltaic battery system. We use a multi-scale multi-physics model of a graphite/lithium iron phosphate (LiFePO4, LFP) cell including solid electrolyte interphase (SEI) formation. The cell-level model is dynamically coupled to a system-level model consisting of photovoltaics (PV), inverter, load, grid interaction, and energy management system, fed with historic weather data. Simulations are carried out for two load scenarios, a single-family house and an office tract, over annual operation cycles with one-minute time resolution. As key result, we show that the charging process causes a peak in degradation rate due to electrochemical charge overpotentials. The main drivers for cell ageing are therefore not only a high state of charge (SOC), but the charging process leading towards high SOC. We also show that the load situation not only influences system parameters like self-sufficiency and self-consumption, but also has a significant impact on battery ageing. We assess reduced charge cut-off voltage as ageing mitigation strategy.
Simulation-based degradation assessment of lithium-ion batteries in a hybrid electric vehicle
(2017)
The insufficient lifetime of lithium-ion batteries is one of the major cost driver for mobile applications. The battery pack in vehicles is one of the most expensive single components that practically must be excluded from premature replacement (i.e., before the life span of the other components end). Battery degradation is a complex physicochemical process that strongly depends on operating condition and environment. We present a simulation-based analysis of lithium-ion battery degradation during operation with a standard PHEV test cycle. We use detailed multiphysics (extended Newman-type) cell models that allow the assessment of local electrochemical potential, species and temperature distributions as driving forces for degradation, including solid electrolyte interphase (SEI) formation [1]. Fig. 1 shows an exemplary test cycle and the predicted resulting spatially-averaged SEI formation rate. We apply a time-upscaling approach to extrapolate the degradation analysis over long time scales, keeping physical accuracy while allowing end-of-life assessment [2]. Results are presented for lithium-ion battery cells with graphite/LFP chemistry. The behavior of these cells in terms of degradation propensity, performance, state of charge and other internal states is predicted during long-term cycling. State of health (SOH) is quantified as capacity fade and internal resistance increase as function of operation time.