Refine
Year of publication
Document Type
- Article (reviewed) (27)
- Conference Proceeding (12)
- Article (unreviewed) (3)
- Report (2)
- Part of a Book (1)
Conference Type
- Konferenzartikel (12)
Is part of the Bibliography
- yes (45)
Keywords
- Plastizität (12)
- Ermüdung (9)
- Mikrostruktur (6)
- Materialermüdung (5)
- Stahl (5)
- Eisenguss (4)
- Simulation (4)
- Thermomechanik (4)
- Finite-Elemente-Methode (3)
- Rissausbreitung (3)
Institute
- Fakultät Maschinenbau und Verfahrenstechnik (M+V) (45) (remove)
Open Access
- Closed Access (20)
- Closed (10)
- Open Access (10)
- Gold (2)
- Diamond (1)
In dem abgeschlossenen Vorhaben „Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Motorbauteilen unter thermisch-mechanischer Ermüdungsbeanspruchung“ der Forschungsvereinigung Verbrennungskraftmaschinen e. V. (FVV) wurde am Fraunhofer Institut für Werkstoffmechanik IWM in Freiburg ein Materialmodell zur Lebensdauervorhersage thermomechanisch belasteter Komponenten entwickelt. Das Modell basiert auf einem viskoplastischen Verformungsmodell für Eisengusswerkstoffe und einem mechanismenbasierten Modell für Mikrorisswachstum zur Lebensdauervorhersage.
Für die Werkstoffe EN GJS700, EN GJV450 und EN GJL250 werden die Lebensdauern unter kombinierter thermomechanischer und hochfrequenter Belastung vorhergesagt. Hierzu wird ein mechanismenbasiertes Lebensdauermodell verwendet, das auf dem Wachstum von Mikrorissen beruht. Das Modell berücksichtigt das Wachstum von Rissen durch nieder- und überlagerte hochfrequente Belastungszyklen. Anhand von einachsigen Ermüdungsversuchen wurden die Parameter des Lebensdauermodells angepasst, sodass eine bestmögliche Lebensdauervorhersage erzielt wird. Dabei stimmen die vorhergesagten Lebensdauern gut mit den experimentell ermittelten Zyklenzahlen zum Versagen überein.
In this paper, the multiaxial formulation of a mechanism-based model for fatigue life prediction is presented whichcan be applied to low-cycle fatigue (LCF) and thermomechanical fatigue (TMF) problems in which high-cycle fa-tigue loadings are superimposed. The model assumes that crack growth is the lifetime limiting mechanism and thatthe crack advance in a loading cycleda/dNcorrelates with the cyclic crack-tip opening displacement ΔCTOD.The multiaxial formulation makes use of fracture mechanics solutions and thus, does not need additional modelparameters quantifying the effect of the multiaxiality. Furthermore, the model includes contributions of HCF on ΔCTODand assesses the effect of the direction of the HCF loadings with respect to LCF or TMF loadings inthe life prediction. The model is implemented into the finite-element program ABAQUS. It is applied to predictthe fatigue life of a thermomechanically loaded notched specimen that should represent the situation between theinlet and outlet bore holes of cylinder heads. A good correlation of the predicted and the measured fatigue lives isobtained.
Für langfaserverstärkte Thermoplaste (LFT) wird ein repräsentatives Volumenelement (RVE) für FEM-Simulationen generiert. Dies geschieht unter Berücksichtigung von mikrostrukturellen Kenngrößen wie Faserorientierungsverteilung, -volumengehalt und -längenverteilung, die für einen charakteristischen Werkstoffzustand experimentell ermittelt wurden. Mittels Mikrostruktursimulationen wird das Kriechverhalten von LFT untersucht. Das viskoelastische Verhalten der Matrix wird experimentell an Substanzproben aus Polypropylen ermittelt und in die RVE-Simulationen mit einem modifizierten Burgers-Modell implementiert. Schließlich werden die Rechnungen mit verschiedenen, fiktiven sowie experimentell ermittelten Faserlängenverteilungen mit Kriechversuchen am LFT verglichen. Es zeigt sich eine starke Abhängigkeit des Kriechverhaltens von der Faserlänge und eine hohe Prognosegüte der Simulationen, die die experimentell ermittelte Längenverteilung berücksichtigen.
In this paper, an unconditionally stable algorithm for the numerical integration and finite-element implementation of a class of pressure dependent plasticity models with nonlinear isotropic and kinematic hardening is presented. Existing algorithms are improved in the sense that the number of equations to be solved iteratively is significantly reduced. This is achieved by exploitation of the structure of Armstrong-Frederik-type kinematic hardening laws. The consistent material tangent is derived analytically and compared to the numerically computed tangent in order to validate the implementation. The performance of the new algorithm is compared to an existing one that does not consider the possibility of reducing the number of unknowns to be iterated. The algorithm is used to implement a time and temperature dependent cast iron plasticity model, which is based on the pressure dependent Gurson model, in the finite-element program ABAQUS. The implementation is applied to compute stresses and strains in a large-scale finite-element model of a three cylinder engine block. This computation proofs the applicability of the algorithm in industrial practice that is of interest in applied sciences.
In this paper the fatigue life of three cast iron materials, namely EN-GJS-700, EN-GJV-450 and EN-GJL-250, is predicted for combined thermomechanical fatigue and high cycle fatigue loading. To this end, a mechanism-based model is used, which is based on microcrack growth. The model considers crack growth due to low frequency loading (thermomechanical and low cycle fatigue) and due to high cycle fatigue. To determine the model parameters for the cast iron materials, fatigue tests are performed under combined loading and crack growth is measured at room temperature using the replica technique. Superimposed high cycle fatigue leads to an accelerated crack growth as soon as a critical crack length and thus the threshold stress intensity factor is exceeded. The model takes this effect into account and predicts the fatigue lives of all cast iron materials investigated under combined loadings very well.
This paper reports on the evolution of cracks in the cylinder heads of a large V8 Diesel engine during cyclic engine tests. The observations are compared with the predictions of a lifetime model for combined thermo-mechanical (TMF) and high cycle fatigue (HCF) loading, which is based on a fracture mechanics analysis of microcrack growth in viscoplastic solids and assumes that the crack advance per cycle is proportional to the cyclic crack tip opening displacement. Since the material of the cylinder heads, the cast iron EN-GJV450, exhibits the typical features of cast iron, namely pressure dependence of the yield stress, dilatancy and tension-compression asymmetry, the Gurson model is applied and combined with the viscoplastic Chaboche model. This constitutive model together with the lifetime model is implemented into a finite element code as a user defined material routine. Published model parameters for the considered cast iron are used to carry out the simulation of the engine test. This simulation comprises a CFD analysis to determine the heat transfer coefficients, a thermal analysis of the load cycle and the mechanical analysis. The thermal analysis reproduces the temperatures at various measuring points sufficiently accurately. Finally, the mechanical analysis predicts the location and orientation of the cracks in the valve bridges correctly in all cases. However, the lifetime predictions are rather conservative compared to the tests (by a factor of 1 to 5 in lifetime). This is discussed and explained by the fact that the cracks were detected in the tests only when they had already spread over a substantial fraction of the valve bridge width. To describe this situation a long-crack analysis would be necessary, which is not yet included in the applied lifetime model.
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In this paper (Part I), the low-cycle fatigue (LCF) and TMF properties of HiSiMo are investigated in uniaxial tests and the damage mechanisms are addressed. On the basis of the experimental results a fatigue life model is developed which is based on elastic, plastic and creep fracture mechanics results of short cracks, so that time and temperature dependent effects on damage are taken into account. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper).
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their life cycle. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In Part I of the paper, a fracture mechanics model for TMF life prediction was developed based on results of uniaxial tests. In this paper (Part II), the model is formulated for three-dimensional stress states, so that it can be applied in a post-processing step of a finite-element analysis. To obtain reliable stresses and (time dependent plastic) strains in the finite-element calculation, a time and temperature dependent plasticity model is applied which takes non-linear kinematic hardening into account. The material properties of the model are identified from the results of the uniaxial test. The plasticity model and the TMF life model are applied to assess the lifetime of an exhaust manifold.