This paper reports on the evolution of cracks in the cylinder heads of a large V8 Diesel engine during cyclic engine tests. The observations are compared with the predictions of a lifetime model for combined thermo-mechanical (TMF) and high cycle fatigue (HCF) loading, which is based on a fracture mechanics analysis of microcrack growth in viscoplastic solids and assumes that the crack advance per cycle is proportional to the cyclic crack tip opening displacement. Since the material of the cylinder heads, the cast iron EN-GJV450, exhibits the typical features of cast iron, namely pressure dependence of the yield stress, dilatancy and tension-compression asymmetry, the Gurson model is applied and combined with the viscoplastic Chaboche model. This constitutive model together with the lifetime model is implemented into a finite element code as a user defined material routine. Published model parameters for the considered cast iron are used to carry out the simulation of the engine test. This simulation comprises a CFD analysis to determine the heat transfer coefficients, a thermal analysis of the load cycle and the mechanical analysis. The thermal analysis reproduces the temperatures at various measuring points sufficiently accurately. Finally, the mechanical analysis predicts the location and orientation of the cracks in the valve bridges correctly in all cases. However, the lifetime predictions are rather conservative compared to the tests (by a factor of 1 to 5 in lifetime). This is discussed and explained by the fact that the cracks were detected in the tests only when they had already spread over a substantial fraction of the valve bridge width. To describe this situation a long-crack analysis would be necessary, which is not yet included in the applied lifetime model.
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their life cycle. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In Part I of the paper, a fracture mechanics model for TMF life prediction was developed based on results of uniaxial tests. In this paper (Part II), the model is formulated for three-dimensional stress states, so that it can be applied in a post-processing step of a finite-element analysis. To obtain reliable stresses and (time dependent plastic) strains in the finite-element calculation, a time and temperature dependent plasticity model is applied which takes non-linear kinematic hardening into account. The material properties of the model are identified from the results of the uniaxial test. The plasticity model and the TMF life model are applied to assess the lifetime of an exhaust manifold.
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In this paper (Part I), the low-cycle fatigue (LCF) and TMF properties of HiSiMo are investigated in uniaxial tests and the damage mechanisms are addressed. On the basis of the experimental results a fatigue life model is developed which is based on elastic, plastic and creep fracture mechanics results of short cracks, so that time and temperature dependent effects on damage are taken into account. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper).