Refine
Year of publication
Document Type
- Article (reviewed) (12)
- Conference Proceeding (6)
- Article (unreviewed) (1)
- Report (1)
Conference Type
- Konferenzartikel (6)
Has Fulltext
- no (20)
Is part of the Bibliography
- yes (20)
Keywords
- Plastizität (6)
- Stahl (5)
- Ermüdung (3)
- Mikrostruktur (3)
- Thermomechanik (3)
- Finite-Elemente-Methode (2)
- Hochtemperatur (2)
- Maschinenelement (2)
- Materialermüdung (2)
- thermomechanische Ermüdung (2)
Institute
Open Access
- Closed Access (20) (remove)
Significant improvements in module performance are possible via implementation of multi-wire electrodes. This is economically sound as long as the mechanical yield of the production is maintained. While flat ribbons have a relatively large contact area to exert forces onto the solar cell, wires with round cross section reduce this contact area considerably – in theory to an infinitively thin line. Therefore, the local stresses induced by the electrodes might increase to a point that mechanical production yields suffer unacceptably.
In this paper, we assess this issue by an analytical mechanical model as well as experiments with an encapsulant-free N.I.C.E. test setup. From these, we can derive estimations for the relationship between lay-up accuracy and expected breakage losses. This paves the way for cost-optimized choices of handling equipment in industrial N.I.C.E.-wire production lines.
Ein tiefgreifendes Verständnis des zyklischen Plastizitätsverhaltens metallischer Werkstoffe ist sowohl für die Optimierung der Materialeigenschaften als auch für die industrielle Auslegung und Fertigung von Bauteilen von hoher Relevanz. Insbesondere moderne Legierungen wie Duplex-Stähle zeigen unter Lastumkehr aufgrund des komplexen mehrphasigen Gefüges sowie der Neigung zu verschiedenen Ausscheidungsreaktionen einen ausgeprägten Bauschinger-Effekt, welcher bei technischen Umformvorgängen berücksichtigt werden muss. Der Bauschinger-Effekt begründet sich maßgeblich in der Entstehung von Rückspannungen, welche aus dem unterschiedlichen Plastizitätsverhalten der austenitischen und ferritischen Phase resultieren. Instrumentierte Mikroindenter-Versuche in ausgewählten Ferrit- und Austenitkörnern haben gezeigt, dass austenitische Gefügebestandteile durch einen deutlich früheren Fließbeginn sowie eine stärkere Rückplastifizierung während der Entlastung charakterisiert sind. Zudem wurde nachgewiesen, dass Ausscheidungen im Rahmen einer 475°C-Versprödung diesen Phasenunterschied verstärken und somit in einem höheren Bauschinger-Effekt resultieren.
The work focuses on predictive capabilities of fundamental cyclic plasticity and fatigue life models, which can be calibrated using limited amount of experiments as specific ones needed for more advanced models are often absent. The analyses are conducted for the synthetic case of exhaust manifold made from cast iron. The thermal boundary conditions from the forced convection were obtained from the computational fluid dynamics considered as a conjugate heat transfer problem. Two rate-independent and temperature-dependent material models were calibrated for structural analyses. Both were validated with experiments on isothermal and anisothermal levels. Sequential thermal–mechanical finite element simulations were performed. Two fatigue life models were employed. The first was a temperature-dependent strain-based fatigue life criterion calibrated from uniaxial data. The second was a temperature-independent energy-based fatigue life criterion resulting in twice lower life than the strain-based criterion, while none of the plasticity models made a significant difference in that prediction.
Due to higher combustion chamber temperatures and pressures in efficient combustion engines, both the high-cycle and thermomechanical fatigue loads on service life-critical components, such as the cylinder head, are increasing. Material comparisons and analysis of damage behavior are very expensive and time-consuming using component tests. This study therefore develops a test method for cylinder head materials that takes into account the combined loading conditions from the above-mentioned loads and allows realistic temperature transients and gradients on near-component samples. The near-component cylinder head sample represents the failure-critical exhaust valve crosspiece and is tested in a test rig specially designed with the aid of conjugate heat transfer simulations. In the test rig, the sample is subjected to thermal stress by a hot gas burner and to mechanical stress by a high-frequency pulsator. Optical crack detection allows permanent observation of fatigue crack growth and crack closure during the test. Fractographic and metallo-graphic examinations of the fracture areas as well as analyses of the damage patterns show that loads close to engine operation can be set in this way and their influences on the damage can be monitored.
Cyclic micro-bending tests on fcc single crystal Ni-base Alloy 718 cantilevers with different crystal orientations were performed to analyze the influence of activated slip systems on dislocation plasticity, latent hardening and the Bauschinger effect. The investigations indicate that plasticity in single crystal micro-cantilevers is significantly influenced by two phenomena - dislocation interaction and dislocation pile-up at the neutral plane. Both phenomena occur at the same time. Their ratio seems to be determined by the activated slip systems. Slip trace analysis indicates that the activation of only one slip system leads to a strong localization of plasticity to a limited number of parallel slip bands. This results in low dislocation interaction and consequently pronounced pile-ups at the neutral plane. In multi slip orientation, the second slip system leads to activation of significantly more dislocation sources, causing a much earlier and more homogeneous elastic-plastic transition zone. In stress-strain hysteresis loops during bending, pronounced dislocation interaction in multi slip orientation leads to a more pronounced latent hardening. The results suggest that on a microstructural length scale, plasticity behavior is strongly affected by activated slip systems, which determine local dislocation phenomena. Based on the results presented in this paper, a finite element analysis of latent hardening and the Bauschinger effect using a single crystal plasticity model with latent kinematic hardening is presented in Part II.
In this paper, the Bauschinger effect and latent hardening of single crystals are assessed in finite element calculations using a single crystal plasticity model with kinematic hardening. To this end, results of cyclic micro-bending experiments on single crystal Alloy 718 in different crystal orientations (single slip and multi slip) with respect to the loading direction are used to determine the slip system related material properties of the single crystal plasticity model. Two kinematic hardening laws are considered: a kinematic hardening law describing latent hardening and a kinematic hardening law without latent hardening. For the determination of material properties for both hardening laws, a gradient-based optimization method is used. The results show that the different strength levels observed for micro-bending tests on different crystal orientations can only be described with latent kinematic hardening well, whereas the pronounced Bauschinger effect is described well by both kinematic hardening laws. It is concluded that cyclic micro-bending experiments on single crystals using different crystal orientations give an appropriate data base for the determination of the slip system related material properties of the single crystal plasticity model with latent kinematic hardening.
High temperature components in internal combustion engines and exhaust systems must withstand severe mechanical and thermal cyclic loads throughout their lifetime. The combination of thermal transients and mechanical load cycling results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material. Analytical tools are increasingly employed by designers and engineers for component durability assessment well before any hardware testing. The DTMF model for TMF life prediction, which assumes that micro-crack growth is the dominant damage mechanism, is capable of providing reliable predictions for a wide range of high-temperature components and materials in internal combustion engines. Thus far, the DTMF model has employed a local approach where surface stresses, strains, and temperatures are used to compute damage for estimating the number of cycles for a small initial defect or micro-crack to reach a critical length. In the presence of significant gradients of stresses, strains, and temperatures, the use of surface field values could lead to very conservative estimates of TMF life when compared with reported lives from hardware testing. As an approximation of gradient effects, a non-local approach of the DTMF model is applied. This approach considers through-thickness fields where the micro-crack growth law is integrated through the thickness considering these variable fields. With the help of software tools, this method is automated and applied to components with complex geometries and fields. It is shown, for the TMF life prediction of a turbocharger housing, that the gradient correction using the non-local approach leads to more realistic life predictions and can distinguish between surface cracks that may arrest or propagate through the thickness and lead to component failure.
Cast aluminum alloys are frequently used as materials for cylinder head applications in internal combustion gasoline engines. These components must withstand severe cyclic mechanical and thermal loads throughout their lifetime. Reliable computational methods allow for accurate estimation of stresses, strains, and temperature fields and lead to more realistic Thermomechanical Fatigue (TMF) lifetime predictions. With accurate numerical methods, the components could be optimized via computer simulations and the number of required bench tests could be reduced significantly. These types of alloys are normally optimized for peak hardness from a quenched state that maximizes the strength of the material. However due to high temperature exposure, in service or under test conditions, the material would experience an over-ageing effect that leads to a significant reduction in the strength of the material. To numerically account for ageing effects, the Shercliff & Ashby ageing model is combined with a Chaboche-type viscoplasticity model available in the finite-element program ABAQUS by defining field variables. The constitutive model with ageing effects is correlated with uniaxial cyclic isothermal tests in the T6 state, the overaged state, as well as thermomechanical tests. On the other hand, the mechanism-based TMF damage model (DTMF) is calibrated for both T6 and over-aged state. Both the constitutive and the damage model are applied to a cylinder head component simulating several cycles on an engine dynamometer test. The effects of including ageing for both models are shown.
Hot work tools are subjected to complex thermal and mechanical loads during hot forming processes. Locally, the stresses can exceed the material’s yield strength in highly loaded areas as e.g. in small radii in die cavities. To sustain the high loads, the hot forming tools are typically made of martensitic hot work steels. While temperatures for annealing of the tool steels usually lie in the range between 400 and 600 °C, the steels may experience even higher temperatures during hot forming, resulting in softening of the material due to coarsening of strengthening particles. In this paper, a temperature dependent cyclic plasticity model for the martensitic hot work tool steel 1.2367 (X38CrMoV5-3) is presented that includes softening due to particle coarsening and that can be applied in finite-element calculations to assess the effect of softening on the thermomechanical fatigue life of hot work tools. To this end, a kinetic model for the evolution of the mean size of secondary carbides based on Ostwald ripening is coupled with a cyclic plasticity model with kinematic hardening. Mechanism-based relations are developed to describe the dependency of the mechanical properties on carbide size and temperature. The material properties of the mechanical and kinetic model are determined on the basis of tempering hardness curves as well as monotonic and cyclic tests.
In this paper, the temperature dependent cyclic mechanical properties of the martensitic hot work tool steel 1.2367 after tempering are investigated. To this end, hardness measurements as well as monotonic and cyclic tests at temperatures in the range from room temperature to 650 °C are performed on material tempered for different tempering times and temperatures. To describe the observed time and temperature dependent softening during tempering a kinetic model for the evolution of the mean size of secondary carbides based on Ostwald ripening is developed. Furthermore, mechanism-based as well as phenomenological relations for the cyclic mechanical properties of the Ramberg-Osgood model depending on carbide size and temperature are introduced. A good overall agreement of the measured and the calculated stress-strain hysteresis loops for different temperatures and heat treatments is obtained using the determined material properties of the kinetic and mechanical model.
In this paper fatigue crack closure under in-phase and out-of-phase thermomechanical fatigue (TMF) loading is studied using a temperature dependent strip yield model. It is shown that fatigue crack closure is strongly influenced by the phase relation between mechanical loading and temperature, if the temperature difference goes along with a temperature dependence of the yield stress. In order to demonstrate the effect of the temperature dependent yield stress, the influence of in-phase and out-of-phase TMF loading is studied for a polycrystalline nickel-base superalloy. By using a mechanism based lifetime model, implications for fatigue lives are demonstrated.
In this paper, the correlation of the cyclic J-integral, ΔJ, and the cyclic crack-tip opening displacement, ΔCTOD, is studied in the presence of crack closure to assess the question if ΔJ describes the crack-tip opening displacement in this case. To this end, a method is developed to evaluate ΔJ numerically within finite-element calculations. The method is validated for an elastic–plastic material that exhibits Masing behavior. Different strain ranges and strain ratios are considered under fully plastic cyclic conditions including crack closure. It is shown that the cyclic J-integral is the parameter to determine the cyclic crack-tip opening displacement even in cases where crack closure is present.
This paper reports on the evolution of cracks in the cylinder heads of a large V8 Diesel engine during cyclic engine tests. The observations are compared with the predictions of a lifetime model for combined thermo-mechanical (TMF) and high cycle fatigue (HCF) loading, which is based on a fracture mechanics analysis of microcrack growth in viscoplastic solids and assumes that the crack advance per cycle is proportional to the cyclic crack tip opening displacement. Since the material of the cylinder heads, the cast iron EN-GJV450, exhibits the typical features of cast iron, namely pressure dependence of the yield stress, dilatancy and tension-compression asymmetry, the Gurson model is applied and combined with the viscoplastic Chaboche model. This constitutive model together with the lifetime model is implemented into a finite element code as a user defined material routine. Published model parameters for the considered cast iron are used to carry out the simulation of the engine test. This simulation comprises a CFD analysis to determine the heat transfer coefficients, a thermal analysis of the load cycle and the mechanical analysis. The thermal analysis reproduces the temperatures at various measuring points sufficiently accurately. Finally, the mechanical analysis predicts the location and orientation of the cracks in the valve bridges correctly in all cases. However, the lifetime predictions are rather conservative compared to the tests (by a factor of 1 to 5 in lifetime). This is discussed and explained by the fact that the cracks were detected in the tests only when they had already spread over a substantial fraction of the valve bridge width. To describe this situation a long-crack analysis would be necessary, which is not yet included in the applied lifetime model.
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their service life. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In this paper (Part I), the low-cycle fatigue (LCF) and TMF properties of HiSiMo are investigated in uniaxial tests and the damage mechanisms are addressed. On the basis of the experimental results a fatigue life model is developed which is based on elastic, plastic and creep fracture mechanics results of short cracks, so that time and temperature dependent effects on damage are taken into account. The model can be used to estimate the fatigue life of components by means of finite-element calculations (Part II of the paper).
HiSiMo cast irons are frequently used as material for high temperature components in engines as e.g. exhaust manifolds and turbo chargers. These components must withstand severe cyclic mechanical and thermal loads throughout their life cycle. The combination of thermal transients with mechanical load cycles results in a complex evolution of damage, leading to thermomechanical fatigue (TMF) of the material and, after a certain number of loading cycles, to failure of the component. In Part I of the paper, a fracture mechanics model for TMF life prediction was developed based on results of uniaxial tests. In this paper (Part II), the model is formulated for three-dimensional stress states, so that it can be applied in a post-processing step of a finite-element analysis. To obtain reliable stresses and (time dependent plastic) strains in the finite-element calculation, a time and temperature dependent plasticity model is applied which takes non-linear kinematic hardening into account. The material properties of the model are identified from the results of the uniaxial test. The plasticity model and the TMF life model are applied to assess the lifetime of an exhaust manifold.
In this paper, an unconditionally stable algorithm for the numerical integration and finite-element implementation of a class of pressure dependent plasticity models with nonlinear isotropic and kinematic hardening is presented. Existing algorithms are improved in the sense that the number of equations to be solved iteratively is significantly reduced. This is achieved by exploitation of the structure of Armstrong-Frederik-type kinematic hardening laws. The consistent material tangent is derived analytically and compared to the numerically computed tangent in order to validate the implementation. The performance of the new algorithm is compared to an existing one that does not consider the possibility of reducing the number of unknowns to be iterated. The algorithm is used to implement a time and temperature dependent cast iron plasticity model, which is based on the pressure dependent Gurson model, in the finite-element program ABAQUS. The implementation is applied to compute stresses and strains in a large-scale finite-element model of a three cylinder engine block. This computation proofs the applicability of the algorithm in industrial practice that is of interest in applied sciences.
In this paper the fatigue life of three cast iron materials, namely EN-GJS-700, EN-GJV-450 and EN-GJL-250, is predicted for combined thermomechanical fatigue and high cycle fatigue loading. To this end, a mechanism-based model is used, which is based on microcrack growth. The model considers crack growth due to low frequency loading (thermomechanical and low cycle fatigue) and due to high cycle fatigue. To determine the model parameters for the cast iron materials, fatigue tests are performed under combined loading and crack growth is measured at room temperature using the replica technique. Superimposed high cycle fatigue leads to an accelerated crack growth as soon as a critical crack length and thus the threshold stress intensity factor is exceeded. The model takes this effect into account and predicts the fatigue lives of all cast iron materials investigated under combined loadings very well.
Für die Werkstoffe EN GJS700, EN GJV450 und EN GJL250 werden die Lebensdauern unter kombinierter thermomechanischer und hochfrequenter Belastung vorhergesagt. Hierzu wird ein mechanismenbasiertes Lebensdauermodell verwendet, das auf dem Wachstum von Mikrorissen beruht. Das Modell berücksichtigt das Wachstum von Rissen durch nieder- und überlagerte hochfrequente Belastungszyklen. Anhand von einachsigen Ermüdungsversuchen wurden die Parameter des Lebensdauermodells angepasst, sodass eine bestmögliche Lebensdauervorhersage erzielt wird. Dabei stimmen die vorhergesagten Lebensdauern gut mit den experimentell ermittelten Zyklenzahlen zum Versagen überein.
In dem abgeschlossenen Vorhaben „Entwicklung von Rechenmodellen zur Lebensdauervorhersage von Motorbauteilen unter thermisch-mechanischer Ermüdungsbeanspruchung“ der Forschungsvereinigung Verbrennungskraftmaschinen e. V. (FVV) wurde am Fraunhofer Institut für Werkstoffmechanik IWM in Freiburg ein Materialmodell zur Lebensdauervorhersage thermomechanisch belasteter Komponenten entwickelt. Das Modell basiert auf einem viskoplastischen Verformungsmodell für Eisengusswerkstoffe und einem mechanismenbasierten Modell für Mikrorisswachstum zur Lebensdauervorhersage.